ACP Manufacturer

Macromolecule Adhesive Film

Macromolecule Adhesive Film


We use the DuPont material to develop and manufacture the Macromolecule adhesive film, such production is application used in ACP production, the application of adhesive film has solved the peel strength problem and difficult lamination problems, the usage of adhesive film in the continuous lamination production has instead of sheet by sheet production in glue connection. The activity not only improve greatly of the peel strength but also save the cost. The technology has get rid of the situation that few countries control the key technology, give the technical support for ACP industry fast development.


  • Thickness: 0.03mm, 0.05mm

  • Width: 500mm-2050mm

  • Content: 60%

  • Compose: DUPONT macromolecule material

  • Density: 0.94

  • Melting point: 90 degree

  • Composite temperature: 125℃-145℃ (according to equipment real temperature)

  • Peeling Strength: ≥8N/mm (GB/T 2790-1995;180°)

  • Elongation at break: ≥300

  • Tensile Strength: ≥7Mpa

  • Adhesion Condition:Working Pressure & time: 3.5-6kg/cm2, 35-60s



Q: What is a film adhesive composite?

A: A film adhesive composite is a type of material used in manufacturing that consists of layers of adhesive films and reinforcing fibers or fabrics.

Q: How thick is film adhesive?

A: The thickness of film adhesive can vary depending on the specific product and application, but it typically ranges from 0.001 to 0.010 inches (0.0254 to 0.254 millimeters).

Q: How thick is HDPE film?

A: The thickness of HDPE (High-Density Polyethylene) film can vary depending on the specific product and intended use, but it typically ranges from 0.5 to 10 mils (0.0127 to 0.254 millimeters).

Q: How do you measure adhesive thickness?

A: Adhesive thickness can be measured using various methods, including micrometer measurements, optical profilometry, and non-destructive testing techniques such as ultrasonic testing or X-ray fluorescence. The specific method used will depend on the adhesive and the desired level of accuracy.